Counterweight iron Lump Counterweight iron Lump Iron 90%minItemCHEMICAL PROPERTIES % maxCast Iron ScrapCSiMnPSZ14-Z343.3-4.51.60-3.200.5-0.80.05-0.100.03-0.05 Weight: 5-25Kg
Counterweight iron sand Counterweight iron Lump Iron 90%minItemCHEMICAL PROPERTIES % maxCast Iron ScrapCSiMnPSZ14-Z343.3-4.51.60-3.200.5-0.80.05-0.100.03-0.05 Spec:sand ,sho
Riser heat insulation agent Riser heat insulation agent Chemcial Content (%)SiO2Al2O3Fe2O3CaOC18-2010-1312-1511-1415-18Physical propertiesMelting point°cSwellness %SizeMoist
Carbon additive for Special Foundry Carbon additive for Special Foundry ZGF 95001Chemical Compositions%F.CAshV.MSMoisture93-961.0max260.01max1.0maxSize:3-10mm 90%minPacking:20Kg paper b
RESICA deoxidation Briquettes Supply:RESICA deoxidation BriquettesRe: 19-20% Si: 35-40%Above as users requirement Re Si contents.Ca:6-8%Mg:5-8%Mn:6%maxS:0.05%maxP:0.06%maxFeBalanc
Carbon Briquettes Supply: Carbon Briquettes for steel making with carbon F.C:93-96% as users requirement carbon contents. Ash:1-2% V.M:1-3% S:0.05-0.1% Moisture:1.0%ma
Carbon additive and REFEMGSI Nodulizer Stock GPC Carbon additive F.CAshV.MSMoisture98.9min1.0max0.1max0.03max0.5max Size:0.5-5mm Packing:25Kg bags and 1000Kg bags Quantity: 40MT/MONTH Stock:Tian
Iron package, tundish and ladle insulation agent Iron package, tundish and ladle insulation agent ItemC %Melting point °cSizeChemcial Content (%)SiO2CaOAl2O3Ladle coverture10-201200-1300+100 me
Ceramic Moulding sand for foundry Ceramic Moulding sand for foundry Al2O3≥75% Fe2O3≤5% Tio2 :2.5%-3.5% SiO2 :8-12% Bulk density: 1.9-2.1g/cm3 Refractoriness: 1800 min oC Sha
Alumina hollow ball heat insulation castable mater Alumina hollow ball heat insulation castable SpecAlumina hollow ball heat insulation castableBulk density g/cm3≥110X24H1350-1450Bulk DensityCold c